The synthesis of pure-phase bismuth ferrite in the Bi–Fe–O system under hydrothermal conditions without a mineralizer (CROSBI ID 158800)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Gajović, Andreja ; Šturm, Sašo ; Jančar, Boštjan ; Šantić, Ana ; Žagar, Kristina ; Čeh, Miran
engleski
The synthesis of pure-phase bismuth ferrite in the Bi–Fe–O system under hydrothermal conditions without a mineralizer
Bismuth ferrite, BiFeO3 (BFO), was synthesized in a hydrothermal process without the introduction of any metal cations, other than Fe3+ and Bi3+. For this purpose, a strong organic hydroxide was used for the precipitation of the bismuth and iron salts. With the aim to study the molar range for the production of BFO in the Bi–Fe–O system under hydrothermal conditions, the complexity of the phases appearing after the reaction was investigated. Pure-phase BFO was achieved in the case of a hydrothermal treatment after the co-precipitation of a solution of bismuth and iron salts containing an equimolar ratio of Bi3+ and Fe3+ ions. Various iron and bismuth compounds having different morphologies were achieved by changing the Bi3+: Fe3+ ratios in the reaction, but no other bismuth iron oxide phases were observed. To get a complete picture of the compounds, we compared the results from transmission electron microscopy (TEM) with those from X-ray powder diffraction, energy-dispersive X-ray spectroscopy (EDXS) and scanning electron microscopy (SEM). The dielectric properties of the pure BFO and a multiphase system were compared. The pure BFO shows a higher dielectric permittivity than the multiphase system and is comparable with the values reported in the literature.
bismuth ferrite ; hydrothermal synthesis ; TEM ; SEM ; XRD
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
93 (10)
2010.
3173-3179
objavljeno
0002-7820
1551-2916
10.1111/j.1551-2916.2010.03882.x