Synthesis and characterization of pack cemented aluminide coating on stainless steel (CROSBI ID 591198)
Prilog sa skupa u zborniku | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Rede, Vera ; Mioč, Boro ; Ćurković, Lidija ; Majić Renjo, Marijana
engleski
Synthesis and characterization of pack cemented aluminide coating on stainless steel
The aluminized coating on the X2CrNi19-11 austenitic stainless steel was produced by a pack cementation method at 1000 °C for 4 hours. For aluminizing process the following mixture of powders was used: aluminum in the form of fine powder applied to the substrate surface, AlCl3 as an activator and corundum (-Al2O3) as an inert filler in powder form to prevent sintering of powder mixtures at high temperatures. Aluminized sample was annealed in two 60-minutes cycles at 700 °C in oxidizing atmosphere. Microhardness HV 0.025 of bulk material and the aluminized coating was measured after aluminization and oxidation. Optical microscopy was used to investigate the microstructure and to measure the thickness of the coatings.
austenitic stainless steel; high temperature aluminizing; oxidation.
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o prilogu
107-109.
2012.
objavljeno
Podaci o matičnoj publikaciji
4th International Scientific and Expert Conference "Technique, Education, Agriculture & Management" (TEAM 2012) : proceedings
Živić, Marija ; Galeta, Tomislav
Slavonski Brod: Strojarski fakultet Sveučilišta u Slavonskom Brodu
1847-9065
Podaci o skupu
International Scientific and Expert Conference "Technique, Education, Agriculture & Management" (4 ; 2012)
poster
17.10.2012-19.10.2012
Slavonski Brod, Hrvatska