Heat treatment influence on clad dissimilar joints weakness
The dissimilar specimens (ASTM A387 Gr.12 + ASTM A240 TP 304L) clad by different procedures (explosion welding, submerged arc welding– surfacing using strip electrode (SAW) and hot rolling) were heat treated (650 °C through 2 hours). The shear strength testing of clad joints and Charpy impact energy testing were performed. The statistical analysis of testing results was elaborated, and the significance of heat treatment influences on the clad joints weakness was established.
clad joints ; heat treatment ; shear strength
nije evidentirano
engleski
Heat treatment influence on clad dissimilar joints weakness
The dissimilar specimens (ASTM A387 Gr.12 + ASTM A240 TP 304L) clad by different procedures (explosion welding, submerged arc welding– surfacing using strip electrode (SAW) and hot rolling) were heat treated (650 °C through 2 hours). The shear strength testing of clad joints and Charpy impact energy testing were performed. The statistical analysis of testing results was elaborated, and the significance of heat treatment influences on the clad joints weakness was established.
clad joints ; heat treatment ; shear strength
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
21 (5)
2014.
1035-1040
objavljeno
1330-3651
1848-6339