Cavitation damages morphology of high-strength low-alloy steel (CROSBI ID 226938)

Prilog u časopisu | prethodno priopćenje | međunarodna recenzija

Aleksić, V. ; Dojčinović, Miroslava ; Milović, Lj. ; Samardžić, Ivan Cavitation damages morphology of high-strength low-alloy steel // Metalurgija, 55 (2016), 3; 423-425

Podaci o odgovornosti

Aleksić, V. ; Dojčinović, Miroslava ; Milović, Lj. ; Samardžić, Ivan

engleski

Cavitation damages morphology of high-strength low-alloy steel

This paper presents the research into behaviour of HSLA steel affected by cavitation. The parent material (PM) and simulated heat-affected zone (SHAZ) were studied. Ultrasonic vibratory cavitation test was performed in laboratory conditions (by stationary specimen method). Scanning electron microscopy (SEM) was used to observe the variations in the surface morphology that occurred within different time intervals.

HSLA steel ; cavitation damage ; SHAZ ; surface ; time of testing

Rad/časopis indeksiran je i u slijedećim bazama : Electronics & Communications Abstracts ; Engineered Materials ; Engineering Research Database ; Materials Business File ; Mechanical & Transportation Engineering Abstracts ; Metals Science ; Solid State and Superconductivity Abstracts i Weldasearch.

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

55 (3)

2016.

423-425

objavljeno

0543-5846

1334-2576

Povezanost rada

Strojarstvo

Poveznice
Indeksiranost