Influence of PANI layer protonation degree on corrosion protection of steel (CROSBI ID 130335)

Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija

Kraljić Roković, Marijana ; Kalić, Marijana ; Duić, Ljerka Influence of PANI layer protonation degree on corrosion protection of steel // Chemical and biochemical engineering quarterly, 21 (2007), 1; 59-64

Podaci o odgovornosti

Kraljić Roković, Marijana ; Kalić, Marijana ; Duić, Ljerka

engleski

Influence of PANI layer protonation degree on corrosion protection of steel

The aim of this work was to study protecting properties of polyaniline (PANI) layers of different degrees of protonation on stainless steel immersed in 0.1 mol dm-3 NaCl solution. Methods of testing were open circuit potential monitoring, and electrochemical impedance spectroscopy. Different degrees of PANI protonation were obtained by keeping stainless steel covered with PANI layer during one day time in solutions of different pH values. The testing solutions were 3 mol dm-3 phosphoric acid solution (pH=0.4), and buffer solutions of pH=4.3 and pH=7.8. Although all PANI layers were tested in the same solution of 0.1 mol dm-3 NaCl, depending on a degree of previously achieved protonation, different protection time of steel samples was obtained. The best protecting properties were obtained for steel covered with the PANI layer kept during one day in the buffer solution of pH=7.8 , before testing, where a complete deprotonation was achieved. The results obtained point out that PANI, under those conditions, presents a physical barrier to the ingress of chloride ions into the passive film, and the electrochemical mechanism of protection is not significantly involved.

polyaniline ; electrochemical synthesis ; stainless steel ; chlorides ; corrosion protection

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

nije evidentirano

Podaci o izdanju

21 (1)

2007.

59-64

objavljeno

0352-9568

1846-5153

Povezanost rada

Kemija, Kemijsko inženjerstvo

Poveznice