CP Ti fabricated by low temperature extrusion of HDH powder: application in dentistry (CROSBI ID 230810)
Prilog u časopisu | izvorni znanstveni rad | međunarodna recenzija
Podaci o odgovornosti
Balog, Martin ; Viskić, Joško ; Krizik, Peter ; Schauperl, Zdravko ; Šnajdar, Mateja ; Stanec, Zlatko ; Ćatić, Amir
engleski
CP Ti fabricated by low temperature extrusion of HDH powder: application in dentistry
Powder metallurgy (PM) commercial purity titanium (CP Ti) was fabricated and studied, with an aim of utilization for dental application. PM CP Ti was manufactured using a cost effective approach, where affordable hydrogenation–dehydrogenation (HDH) process Ti 99.4 wt.% powder was consolidated via the following sequence of PM techniques: cold isostatic pressing, warm vacuum pressing at 420 °C and warm direct extrusion at 500 °C. The paper presents the first studies on processing, microstructure, testing of mechanical properties, fatigue performance and bonding strength with different veneer coatings. By employed consolidation process sound material with low porosity (1.5%) and sustained oxygen content (0.21 wt.%) was attained. The tensile properties obtained for PM CP Ti (UTS = 701 MPa, YS0.2 = 512 MPa, ε = 13 %) were improved over to those for cast / milled CP Ti Grade 4 reference, the material commonly used in dentistry. Tested using the ISO 14801 standard for dental implants, the samples machined from PM CP Ti showed fatigue performance similar to CP Ti Grade 4. PM CP Ti used as a metal base material in restoration metal – ceramic systems showed very good bond strength with three commercially available veneering ceramics and complied with the ISO 9693 standard. Within the limitations of this paper, the preliminary results demonstrated that performance of economic PM CP Ti is equal or superior to CP Ti Grade 4 reference material and it can be used in prosthodontics.
dentistry ; extrusion ; mechanical properties ; powder metallurgy ; prosthodontic ; titanium ; veneering
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
nije evidentirano
Podaci o izdanju
704
2016.
351-359
objavljeno
1013-9826
1662-9795
10.4028/www.scientific.net/KEM.704.351
Povezanost rada
Dentalna medicina, Metalurgija, Strojarstvo