Effect of different thermo-light polymerization on flexural strength of two glass ionomer cements and a glass carbomer cement

STATEMENT OF PROBLEM: Whether polymerization lights can be used for heating glass ionomer cements (GICs) or glass carbomer (GCP) to improve their mechanical properties is not well established. PURPOSE: The purpose of this in vitro study was to assess the effect of thermo-light polymerization on the flexural strength (FS) of 2 GICs (Fuji IX GP Fast, Ketac Molar) and a GCP. MATERIAL AND METHODS: Specimens (n=10) were prepared in stainless steel molds (2×2×25 mm), compressed, exposed to 3 polymerization lights (500, 1000, 1200 mW/cm2) for 2 cycles of 40 seconds on each side, and stored in petroleum jelly (37°C, 24 hours). RESULTS: Significant FS differences were detected among groups after different thermo-light polymerization regimens (F=50.926, df=11, P<.001). GCP showed the highest mean FS (∼5 times, P<.001) after thermo-light polymerization with power outputs of 1000 (127.1 ±25.8 MPa) and 1200 mW/cm2 (117.4 ±18.5 MPa), with no significance difference between them (P=.98), compared with 500 mW/cm2 (24.1 ±1.7 MPa). For Ketac Molar, compared with autopolymerization setting (15.5 ±3.1 MPa), a significant increase in mean FS (∼2.5 times) was only observed in specimens treated with 1200 mW/cm2 polymerization light (P=.03). For Fuji IX GP Fast, only the light with 1000 mW/cm2 output significantly increased the FS (98.9 ±23.4 MPa, P<.001) compared with the autopolymerization setting (34.9 ±6.4 MPa). CONCLUSIONS: Thermo-light polymerization accelerated the development of FS in the tested GICs, potentially protecting against saliva contamination during the first 3 to 4 minutes after mixing GIC. Thermo-light polymerization of the glass carbomer with power outputs of 1000 and 1200 mW/cm2 also substantially increased FS. The clinical advantages of the findings should be validated by in vivo studies.

glass ionomer ; mechanical properties ; thermo-curing

nije evidentirano